We are stockists of 31803 duplex alloys in sheet, plate, and bar directly distributed globally from our UK stockholding warehouse, combined with our large capacity cutting capabilities we can meet requirements for many industries.
The following are the properties of 31803:
Stainless ferritic-austenitic Cr-Ni-Mo steel with nitrogen addition.
High corrosion resistance, especially against stress corrosion cracking in solutions containing chloride.
Good strength properties.
Resistant to intergranular corrosion in the temperature range up to 300°C.
Heat treatment subsequent to welding not necessary.
Surface condition for optimum corrosion resistance: pickled, heat treated free from scale or machined.
Application
Components in the chemical industry, e.g. separator and heat exchanger parts, from the paper industry, oil and gas production, compressor parts, seawater desalination plants.
Technical Info
Chemical Composition (average %)
| C | Si | Mn | Cr | Mo | Ni | N |
| 0.025 | 0.60 | 1.30 | 22.60 | 3.20 | 5.80 | 0.17 |
Standards
| EN / DIN | ASTM | UNS | AFNOR |
<1.4462 >
X2CrNiMoN22-5-3 | A240 | S31803 | Z2CND22-5 Az |
Hot Forming
Forging
1200 to 950°C / Air cooling
Heat Treatment
Solution annealing:
1020 to 1100°C
Water , air (thickness below 2mm)
Structure
Ferrite + Austenite
Mechanical Properties
Condition: solution annealed
| Product | Dimension
Size
mm | 0.2% proof stress
N/mm2
min. | Tensile strength
N/mm2 | Elongation A5
% min.
L Q T | Impact strength
(ISO-V)
J min.
L Q T |
| St | ≤ 160 | 450 | 650 – 880 | 25 – – – – | 100 – – – – |
| Bl | ≤ 75 | 460 | 640 – 840 | 252) 252) – – | 90 60 – – |
St = Bar ,
Bl = Sheet or plate
L = Longitudinal, Q = Transverse, T = Tangential
1) For sheet or plate < 3mm = A80mm specimen
The values for other products and dimensions shall be established by agreement.
Hight Temperature Properties
Condition: solution annealed
0.2% yield strength
N/mm² min. | Temperature |
| 100°C | 150°C | 200°C | 250°C |
| 360 | 335 | 315 | 300 |
Welding
Good weldability. Welding is possible with all processes usual for stainless steels. We recommend depending on applications electric arc welding with covered electrodes, inert gas welding or SA-welding. Preheating and heat treatment after welding is not necessary. For high stressed heavy walled constructions the limited preheat temperature of 150°C maximum is recommendable. Maximum interpass temperature 150°C. Keep heat input low especially for small wall thicknesses. The TIG-process should be given reference for root welding.
Physical Properties
Thermal conductivity at ……………….. 20°C ………………15.0 ………W/(m.K)
Specific heat at …………………………..20°C ………………500 ……….J/(kg.K)
Electrical resistivity at …………………. 20°C ………………0.80 ………Ohm.mm2/m
Modulus of elasticity at ……………….. 20°C ………………200 x 103 N/mm2
Magnetic properties ……………………………………………..magnetic
Thermal expansion between
20°C and …°C, 10-6 m/(m.K) at | Temperature | 10-6 m/(m.K) |
| 100°C | 13.0 |
| 200°C | 13.5 |
| 300°C | 14.0 |
| Modulus of elasticity, 103 N/mm2 at | Temperature | 103 N/mm2 |
| 20°C | 200 |
| 100°C | 194 |
| 200°C | 186 |
| 300°C | 180 |
As regards applications and processing steps that are not expressly mentioned in this product description/data sheet, the customer shall in each individual case be required to consult us.